Nd:YLF |
|
Abal
OptoTek社 (AOTK)
|
|
Neodymium
doped Yttrium Lithium Fluoride Crystal (Nd:YLF)
YLF
is grown utilizing a advanced modified
Czochralski technique. Nd:YLF offers an
alternative to the more common Nd:YAG host for
near IR operation. The combination of weak
thermal lensing, large fluorescence line width
and naturally polarized oscillation makes
Nd:YLF an excellent material for CW,
modelocked operation.
Advantages of Nd:YLF Crystals
●
High
power, low beam divergence, efficient single
mode operation
●
High
average power Q-switched at a moderate
repetition rate
●
Linear
polarized resonators for Q-switching and
frequency doubling
●
Stimulated
emission cross section and lifetime product is
favorable for low CW threshold
●
1053nm
output matches gain curves of Nd:Glass and
performs well as an oscillator and
pre-amplifier for this host
Basic Properties
Formula |
Nd:
LiYF4 |
Crystal
Structure
|
Tetragonal
|
Space
Group |
I41/a |
Lattice
Parameters
|
a=5.16Å,c=10.85
Å
|
Mohs
Hardness
|
4-5
|
Melting
Point
|
825°C
|
Density
|
3.95
g/cm3
|
Thermal
Conductivity
|
0.06
W /cm°C
|
Heat
Capacity
|
0.79
J g-1 K-1
|
Thermal
Expansion
|
13
x 10-6 °C-1
(along a axis)
8
x 10-6 °C-1
(along c axis)
|
Young’s
Modulus
|
7.65x108
g/cm2
|
Optical
and Special Properties
Transparency
Region
|
180
~ 6700 nm
|
Peak
Stimulated Emission Cross Section |
1.8×10-19
cm2 (E‖c)
at 1047 nm
1.2×10-19 cm2
(E丄c)
at 1053 nm |
Spontaneous
Fluorescence Lifetime |
485μs
for 1% Nd |
Scatter
Losses
|
<0.2%/cm
|
Peak
Absorption Coefficient (for
1.2% Nd)
|
a
=10.8cm-1 (792.0 nm E‖c)
a
=3.59cm-1 (797.0 nm E丄c)
|
Fluorescent
Lifetime
(Nd
1at%) |
230
μs |
Laser
Wavelength
|
1047nm
(‖c,
or a-cut crystal)
1053nm
(丄
c,
or c-cut crystal) nm
|
Index
of Refraction
|
ne
= 1.456,
no
= 1.479
at 525 nm
ne
= 1.448,
no = 1.470
at 1050 nm
|
Therm-optic
Coefficients (dn/dT)
|
-2.44x10
-6/°C,
-0.54x10 -6/°C
at 436 nm
-2.86x10 -6/°C,
-0.91x10 -6/°C
at 578 nm
-4.30x10 -6/°C,
-2.00x10 -6/°C
at 1060 nm
|
Sellmeier
Equations ( λin µm) |
no2
=1.38757+0.70757λ2/(λ2
-0.00931)+0.18849λ2/(λ2
-50.99741)
ne2
=1.31021+0.84903λ2/(λ2
-0.00876)+0.53607λ2/(λ2
-134.9566) |
YLF exhibits tetragonal symmetry with
crystallographic axes a=b≠c,
which are orthogonal ,α=β=g=90°.
YLF is a uniaxial crystal with its optical
axis aligned with the c axis. Our standard
Nd:YLF is grown along the a direction. The π-transition
(E‖c)
occurs at 1047nm with an emission
cross-section 50% greater than the σ-transition
(E丄c)
cross section at 1053nm.
Standard Specifications
Standard
Nd Dopant Concentration |
1.0±0.1% |
Wavefront
Distortion |
≤
0.25λ/inch |
Extinction
Ratio |
≥28
dB |
Rod
Sizes
|
Diameter:
3~15mm, Length: 1~150mm
|
Dimensional
Tolerances
|
Diameter:
+0.00/-0.05mm, Length
+0.5/-0.2 mm
|
Flatness
|
λ/8
@633 nm
|
Parallelism
|
<
10 arc seconds
|
Perpendicularity
|
<
5 arc minutes
|
Surface
Quality
|
10/5
Scratch/Dig per MIL-O-13830A
|
Barrel
Finish
|
50
- 80 micro-inch (RMS)
|
Clear
Aperture
|
>
Central 90%
|
AR
Coatings |
R
< 0.10% @1064 nm per surface |
|
|
|